Indonesia PENGARUH UKURAN PARTIKELTERHADAP SIFAT FISIK DAN MEKANIK KOMPOSIT LIMBAH GERGAJI KAYU JATI  DENGAN MATRIK RESIN EPOXY: PENGARUH UKURAN PARTIKELTERHADAP SIFAT FISIK DAN MEKANIK KOMPOSIT LIMBAH GERGAJI KAYU JATI  DENGAN MATRIK RESIN EPOXY

rita desiasni; Fauzi  Widyawati; Riza Monica

doi:10.36761/hexagon.v3i1.1467

Authors

rita desiasni Universitas Teknologi Sumbawa
Fauzi Widyawati
Riza Monica

DOI:

https://doi.org/10.36761/hexagon.v3i1.1467

Keywords:

Particle size, teak powder, epoxy, physical properties, mechanical properties

Abstract

The physical and mechanical properties of particle composite materials are influenced by particle size. Variations in particle size will form different physical and mechanical properties. The size variations used are 100 mesh, 150 mesh, 200 mesh. The comparison between matrix and particles is 70% : 30% using the hand lay-up method. The test consists of physical tests, namely density and thickness expansion as well as mechanical tests consisting of Modulus Of Rapture (MOR) and Modulus Of Elasticity (MOE). The results of the physical density test were at a value of 0.93-1.02 g/cm³, the best density was at a particle size of 100 mesh with a value of 1.02 g/cm³. While the thickness test obtained values ??ranging from 9.3-9.8%, with the highest thickness development of 9.8% at a particle size of 100 mesh. While the results of the mechanical test itself, all variations in mesh size meet the standard, namely the highest MOR test is obtained in the 100 mesh variation, with a value of 341.15 kgf/cm², while in the MOE test none of which meets the standards of SNI 03-2105-2006, the highest mesh variation is obtained by mesh. obtained at mesh 100 that is 8072.49 kgf/cm².

References

Arzondo, L.M., A. Vazquez, J.M. Carella, and J.M. Pastor. (2004). A low-cost, low-fiber- breakage, injection molding process for long sisal fiber reinforced polypropylene. Polymer Engineering and Science 44: 1766-1772.

Autar, K.KAW. (2006). Mechanics of composites material, second edition. CRC Press: Boca Raton. New York.

Badan Standarisasi Nasional. (2006). Standar Nasional Indonesia SNI 01-4449-2006.

Bambang Subiyanto, Raskita Saragih dan Effendy Husin. (2003). Pemanfaatan Serbuk Serbuk Sabut Kelapa Sebagai Bahan Penyerap Air dan Oli Berupa Panel Papan Partikel. J. Ilmu & Teknologi Kayu 26 Tropis Vol. 1 x No. 1 x 2003.

Bramantyo, A. (2008). Pengaruh Konsentrasi Serat. Skripsi: Universitas Indonesia. Depok.

Budiadji. (2004). Sifat Fisik dan Mekanis Papan Partikel Serabut Buah Kelapa Sawit ( Elais Guinensis Jack ) dengan Campuran Limbah Plastik Jenis PE ( Polyethlene ). Fakultas Kehutanan Unlam. Banjar baru

Budiawan, Muhammad Agus. (2016). Uji Karakteristik Fisis dan Kuat Tekan Papan Komposit Limbah Serbuk Gergaji Kayu Jati Putih Dan Serat Pelepah Pisang. Skripsi : Jurusan Fisika Fakultas Sains dan Teknologi, Universitas Islam Negeri ALaiuddin, Makassar.

Edy Batara Mulya Sireger. (2011). Potensi Budidaya jati. Skripsi, Fakultas Pertanian: Program Studi Kehutanan. Universitas Sumatra Utara.

Haygreen, J.G. dan Jim L. (1996). Hasil hutan dan ilmu kayu, suatu pengantar terjemahan Subjipto A.H, dan Soenardi P., Gadjha Mada University press. Yogyakarta, hal 99-102.

Iswanto AH, Coto Z, Effendi K. (2008). Pengaruh Perendaman Partikel Terhadap Sifat Fisis Dan Mekanis Papan Partikel dari Ampas Tebu (Saccharum officinarum). Jurnal Perennial, 4(1) : 6-9.

Khoirul, H. (2016). Analisis Kekuatan Material Komposit Berpenguat Serat Gelas Untuk Pembuatan Helm Race. Skripsi. Teknik Mesin. Polyteknik Muhammadiyah Yogyakarta.

Kurniawan. (2014). Pengaruh Suhu Dan Perbandingan Katalis Zeolit TerhadapKarakteristik Produk Pirolisis Kayu Jati (Tectona Grandist Lf)” Jurnal Teknik Kimia, h. 217-218.

Lelana. (2005). Pengawetan Bagian Lunak Kayu Kelapa Secara Rendaman Dingin Dengan Bahan Pengawet CCB. Info Hasil Hutan. Vol 11 No.2 Bogor.

Novendra, Yanu. (2008). Karakteristik Biometrik Pohon Jati(Tectona Grandis L.F.)” Skripsi. Bogor: Fakultas Kehutanan.

Nurcahyanto, Hardiman. (2018). Evaluasi Sifat Mekanik High Density Polyethylene Yang diisi Serat Batang Pisang dan Partikel Zeolit ALam, TRAKSI Vol. 18 No. 2 Desember 2018, Majalah Ilmiah Teknik Mesin.

Setyawati, D. (2010). Komposit Serbuk Kayu Plastik Daur Ulang : Teknologi Alternatif Pemanfaatan Limbah Kayu dan Plastik.

Sidabutar, N. R. (2009). Pengaruh Parafin Pada Pembuatan Papan Partikel Serat Acak Serabut Kelapa. Tugas Akhir S-1 : Fakultas MIPA. Universitas Sumatera Utara. Medan.

Surdia, T. (1995). Pengetahuan Bahan Teknik. Jakarta: Pradnya Paramita.

Ulfah, F., Syakbaniah., dan Darvina, Y. (2015). Pengaruh Variasi Komposisi Serat Tandan Kosong Sawit (TKS) dan Serbuk Kayu terhadap Sifat Fisis dan Mekanis Papan Partikel. Pillar of psics: 5:113-120. Universitas Negeri Padang. Padang.

Wahyuningsih, N. S. (2011). Pengaruh Perendaman dan Geometri Partikel tehadap Kualitas Papan Partikel Sekam Padi. Institut Pertanian Bogor. Bogor.