PENGARUH KONSENTRASI NaOH TERHADAP KEKUATAN FISIK, MEKANIK DAN MORFOLOGI KOMPOSIT BERPENGUAT SERBUK KAYU SENGON (Albizia Chinensis) - RESIN EPOXY
DOI:
https://doi.org/10.36761/hexagon.v4i1.2256Keywords:
Kayu sengon, Variasi NaOH, MOE dan MOR, kerapatan, mikrostruktur.Abstract
This study aims to analyze the effect of Non-Treatment and NaOH variations of Sengon 200 mesh wood powder with a volume fraction of 30% powder and 70% resin, with an epoxy resin matrix on the mechanical, physical and microstructural strength. The method of making composites is the hand lay up method with powder and resin materials that have been mixed evenly into a mold that has been coated with a release agent. Physical properties testing of the highest density on powders that received 2% alkalization treatment, which was 0.89 gr/cm3 and the lowest density on Non-Treatment powders, which was 0.80 gr/cm³. The results of the non-treatment MOE mechanical test obtained the lowest test value of 572.3 kgf/cm² and the highest test value of the 2% alkalization treatment, which was 2311.1 kgf/cm². The results of the non-treatment MOR mechanical test, the lowest value was 29.8 kgf/cm² and the highest MOR test value was in the 2% alkalization treatment, which was 87.0 kgf/cm². The results of microstructural testing showed that in the alkalizing 2% NaOH, slightly coarse particles were seen which blended perfectly with the matrix and at least voids were seen. Meanwhile, in the non-treatment powder, the particles do not blend well and can stick well, this is because the hemicellulose and lignin are waxy layers present in the sawdust.
References
Setyanto, S. (2012). Komposit Partikel Serbuk Kayu Dengan Resin Urea Formaldehid sebagao bahan baku utaman Box Speaker.
Statistik, B. P. (2015). Produksi Kayu Hutan Menurut Produksi (m3).
Chandra, R. (2021). Pengararuh Volume limbah serbuk kayu jati ( tectona grandis) terhadap daya serap air pada komposit partikel dengan matriks epoksi. Hexagon, Fakultas teknolosi dan mineral universitas teknologi sumbawa.
Wahyuningsih, N. S. (2011). Pengaruh Perendaman dan Geometri Partikel tehadap Kualitas Papan Partikel Sekam Padi.
Ngadianto A, w. R. (2017). karakteristik Papan Partikel limbah kayu sengon dengan perlakuan pengawetan Asap Cair. Jurnal Nasional Teknologi Terapan, 1-7.
Wardono, A. (2006). Pemanfaatan Serbuk Gergaji Kayu Jati (Tectona Grandis) sebagai Campuran Bahan Pengisi pada Pembuatan Bata beton Pejal.
Ulfah, F. S. (2015). Pengaruh Variasi Komposisi Serbuk Tandan Kosong Sawit (TKS) dan Serbuk Kayu terhadap Sifat Fisis dan Mekanis Papan Partikel. Pillar of psics,, 5:113- 120.
Arif, S. (2019). Karakteristik Sifat Mekanis Disk Pad Komposit Serbuk Kayu Jati–Polyster. Seminar Nasional Teknologi dan Rekayasa (SENTRA).
Ribot, N. M. (2011). Mechanical Properties Of Kenaf Fiber Composite Using Co-Cured In Line Fiber Joint. international Journal. 821–822.
Monica, R. (2020). Pengaruh Ukuran Partikel Terhadap Sifat Fisik dan Mekanik Komposit Limbah Gergaji Kayu Jati dDengan Matriks Epoxy. Hexagon Jurnal teknik dan Sains, 46-52.
Hartanto, L. (2009). Study Perlakuan dan Fraksi Volume Serbuk Terhadap kekuatan Bending, Tarik dan impak komposit berpenguat serbuk ramibermatriks polyster BTQN 157. Tugas Akhir S-1.
Acharya. (dkk). Pengaruh Alkalisasi Komposit Serbuk kelapa-Poliester Terhadap Kekuatan tarik. Vol. 2, No. 2, 123-129.
Maryanti B, S. A. (2011). Pengaruh Alkalisasi Komposit serta kelapa Poliestet terhadap kekuatan Tarik. Jurnal rekaya mesin, vol. 2, no.2, 123-129.
Setyanto, S. (2012). Komposit Partikel Serbuk Kayu Dengan Resin Urea Formaldehid sebagao bahan baku utaman Box Speaker.
Arzondo LM, V. A. (2004). A low-cost, low- fiberbreakage, injection molding process for long sisal fiber reinforced polypropylene. Polymer Engineering and Science.
Hull, D. (2001). An Introduction to Composite Materials.
Iskandar, M. I. (2006). Pemanfaatan Kayu Hutan rakyat Sengon (Parasarianthes Falcatia ) Nielsen untuk kayu Rakitan. 189-193.
Sandi, R. (2009). Pengaruh penambahan Kuat Lentur, Tekan, dan Tarik papan Partikel Dari Serbuk Gergaji Kayu Sengon. Seminar Nasional Aplikasi teknologi Prasarana Wilayah, 293- 297.
Satmoko, M. A. (2013). Pengaruh Variasi Temperatur cetakan Terhadap karakterisasi Briket Kayu Sengon Pada Tekanan Kompaksi 6000 Psig.
Wang, B. (2003). Modifikasi Flax Fiber by Chemical Treament. Presentasi di CSAE/SCGR 2003 Meeting Monteal Quebec.
Shabri, M. (2014). Pengaruh Rasio Epoksi/Ampas Tebu dan Perlakuan Alkali Pada Ampas Tebu Terhadap Kekuatan Bentur Komposit Partikel epoksi Berpengisi Serbuk Ampas Tebu. Departemen Teknik kimia.
Japanese Industrial Standard. (2003). JIS A 5098 Particleboard. Jepan Og Government.
Rusnayanti. (2013). Instrumen Optik Jurusan. Pendidikan Mipa Fakultas Tarbiyah Dan Keguruan Uin Sunan Gunung Djati..
Veni, P. M. (2020). Analisis pangaruh variasi massa papan partikel berlapis batang pisang dan tepurung kelapa terhadap sifat fisik dan mekanik papan partikel perekat resin epoksi . jurnal fisika unand (9) 1, 60-66.
Wahyuningsih, N. S. (2011). Pengaruh Perendaman dan Geometri Partikel tehadap Kualitas Papan Partikel Sekam Padi.
Published
Issue
Section
Copyright (c) 2023 Hexagon Jurnal Teknik dan Sains
This work is licensed under a Creative Commons Attribution 4.0 International License.